Comparative Specifications |
| |
Nominal Chemical Analysis |
| |
Mechanical Properties |
|
| TECHNI-CAST |
MNLA |
MNLB |
MNLC |
MNLD |
MNLE |
IN610 |
IN625 |
HASC |
| FEDERAL |
QQ-N-288, Comp. A |
QQ-N-288, Comp. B |
QQ-N-288, Comp. C |
QQ-N-288, Comp. D |
QQ-N-288, Comp. E |
|
|
|
| QQ-C-551 |
|
|
|
|
|
|
|
| MILITARY |
MIL-C-15345g, #18 |
MIL-C-15345g, #16 |
MIL-C-15345g, #26 |
MIL-C-15345g, #17 |
MIL-C-15345g, #19 |
|
|
|
| MIL-N-20164 |
MIL-N-20165, Gr. A |
|
MIL-N-20165, Gr. B |
|
|
|
|
|
MIL-N-4498, Gr. I |
|
MIL-N-4498, Gr. II |
|
|
|
|
| NAVY |
46M1g |
46N7, CI. A |
|
46N7, CI. B |
|
|
|
|
| ASTM |
A-494, M35-1 |
A-494, M30H |
|
A-494, M25S |
A-494, M30C |
A-494, CY40 |
A-494, CW6MC |
A-494, CW12MW |
| A-494, M35-2 |
|
|
|
|
|
|
|
| SAE |
|
|
|
|
|
|
|
|
| AMS |
|
|
|
4892 |
|
|
|
|
| COPPER |
31.00 |
31.00 |
30.00 |
30.00 |
31.00 |
|
|
|
| ZINC |
|
|
|
|
|
|
|
|
| IRON |
.75 |
1.00 |
1.25 |
1.25 |
1.00 |
|
|
|
| SILICON |
1.75 |
3.25 |
3.75 |
4.25 |
1.75 |
3.00X |
1.00X |
1.00X |
| NICKEL |
65.75 |
64.00 |
64.00 |
63.50 |
64.00 |
BAL |
BAL |
BAL |
| COBALT |
|
|
|
|
|
|
|
|
| MANGANESE |
.75 |
.75 |
1.00 |
1.00 |
.75 |
1.50X |
1.00X |
1.00X |
| BERYLLIUM |
|
|
|
|
|
|
|
|
| NIOBIUM |
|
|
|
|
1.50 |
|
4.00 |
|
| CHROMIUM |
|
|
|
|
|
15.50 |
21.50 |
16.50 |
| IRON |
|
|
|
|
|
11.00X |
5.00X |
6.00 |
| TUNGSTEN |
|
|
|
|
|
|
|
4.50 |
| VANADIUM |
|
|
|
|
|
|
|
0.30 |
| MOLYBDENUM |
|
|
|
|
|
|
9.00 |
17.00 |
| TENSILE STRENGTH psi |
75,000 |
115,000 |
130,000 |
|
75,000 |
|
|
|
| YIELD STRENGTH psi |
40,000 |
70,000 |
90,000 |
|
40,000 |
|
|
|
| ELONGATION % |
35 |
15 |
12 |
|
35 |
|
|
|
| HARDNESS, BRINELL |
141 |
250 |
276 |
332 |
141 |
|
|
|
| CONDITION |
AC |
AC |
AC |
AC |
AC |
|
|
|
|
|
|
|