Comparative Specifications |
| |
Nominal Chemical Analysis |
| |
Mechanical Properties |
|
| TECHNI-CAST |
A043 |
A195 |
A214 |
A319 |
A355 |
A356 |
A354 |
A535 |
TENZ |
| FEDERAL |
QQ-A-601c, Alloy 43 |
QQ-A-601c, Alloy 195 |
QQ-A-601c, Alloy 214 |
QQ-A-601c, Alloy 319 |
QQ-A-601c, Alloy 355 |
QQ-A-601c, Alloy 356 |
|
|
QQ-A-601c, Tenzaloy |
| QQ-A-601a, Comp. 2 |
QQ-A-601a, Comp. 4 |
QQ-A-601a, Comp. 5 |
QQ-A-601a, Comp. 18 |
QQ-A-601a, Comp. 10 |
QQ-A-601a, Comp. 3 |
|
|
QQ-A-601b, CI. 22M |
| QQ-A-596d, Alloy 43 |
|
|
QQ-A-596d, Alloy 319 |
QQ-A-596d, Alloy 355 |
QQ-A-596d, Alloy 356 |
|
|
QQ-A-596d, Tenzaloy |
| QQ-A-596a, Comp. 7 |
|
|
QQ-A-596a, Comp. 11 |
QQ-A-596a, Comp. 6 |
QQ-A-596a, Comp. 8 |
|
|
QQ-A-596c, CI. 20 |
| MILITARY |
MIL-A-17129, CI. 2 |
MIL-A-17129, CI. 4 |
MIL-A-17129, CI. 5 |
|
MIL-A-17129, CI. 7 |
MIL-A-17129, CI. 3 |
MIL-A-21180C, |
|
MIL-A-17129, CI. 8 |
|
|
|
|
|
|
Alloy 354 |
|
MIL-A-12033, |
|
|
|
|
|
|
|
|
Comp. 1 & 2 |
| NAVY |
46A1f , CI. 2 |
46A1f, CI.4 |
46A1f, CI. 5 |
|
46A1f, CI.7 |
46A1f, CI.3 |
|
|
|
| ACI |
|
|
|
|
|
|
|
|
|
| ASTM |
B-26, S5A |
B-26, C4A |
B-26, G4A |
B-26, 319.0 |
B-26, 355.0 |
B-26, A356.0 |
|
B-26, 535.0 |
B-26, 713.0 |
| B-26, S5B |
|
|
B-26, SC64D |
B-26, SC51A |
B-26, SG70A |
|
|
|
| B-108, S5A |
|
|
B-108, SC64D |
B-108, SC51A |
B-108, SG70A |
|
|
B-26, ZC81A |
| B-108, S5B |
|
|
|
B-108, SC51B |
|
|
|
B-108, ZC81B |
| SAE |
35 |
38 |
320 |
329 |
322 |
323 |
|
535 |
315 |
|
|
|
326 |
|
|
|
|
|
| AMS |
|
|
4230 |
|
4210 |
4217 |
|
|
|
|
|
4231 |
|
4212 |
|
|
|
|
|
|
|
|
4214 |
|
|
|
|
|
|
|
|
4280 |
|
|
|
|
|
|
|
|
4281 |
|
|
|
|
| Aluminum |
95.00 |
94.50 |
96.00 |
90.50 |
92.25 |
92.65 |
88.70 |
|
91.40 |
| Silicon |
5.00 |
1.00 |
4.00 |
6.00 |
6.00 |
7.00 |
9.00 |
0.15 |
|
| Copper |
|
4.50 |
|
3.50 |
1.25 |
|
1.80 |
0.05 |
.70 |
| Magnesium |
|
|
|
|
.50 |
.35 |
.50 |
6.60 |
.40 |
| Manganese |
|
|
|
|
|
|
|
0.20 |
|
| Titanium |
|
|
|
|
|
|
|
0.20 |
|
| Tensile Strength, psi |
23,000 |
33,000 |
26,000 |
34,000 |
42,000 |
38,000 |
55,000 |
35,000 |
40,000 |
|
38,000 |
|
40,000 |
|
|
|
|
|
| Yield Strength, psi |
9,000 |
17,000 |
14,000 |
19,000 |
27,000 |
30,000 |
41,000 |
18,000 |
28,000 |
|
25,000 |
|
27,000 |
|
|
|
|
|
| Elongation, % |
10 |
9 |
10 |
2.5 |
4 |
5 |
6 |
9 |
6 |
|
6 |
|
3.5 |
|
|
|
|
|
| Reduction of Area, % |
|
|
|
|
|
|
|
|
|
| Hardness, Brinell |
50 |
70 |
50 |
85 |
100 |
95 |
105 |
70 |
75 |
|
85 |
|
95 |
|
|
|
|
|
| Condition |
F |
T4 |
F |
F |
T6 |
T6 |
T61 |
F |
T5 |
|
T6 |
|
T6 |
|
|
|
|
|
|
|
|
|